Conductivity study in PEO-LiOAc based polymer electrolyte
Polyethylene oxide (PEO) films doped with lithium acetate (LiOAc) were prepared by the solution cast technique. The molecular weight of PEO was 300 000 g mol(-1). Lithium acetate was added to PEO in different weight ratios ranging from 0 to 30 wt-%. The PEO-LiOAc mixtures were dissolved in 1% acetic...
Saved in:
| Main Authors: | , , |
|---|---|
| 格式: | Article |
| 出版: |
Springer Verlag (Germany)
2009
|
| 主題: | |
| 在線閱讀: | http://eprints.um.edu.my/7643/ https://doi.org/10.1179/143307509X440532 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Polyethylene oxide (PEO) films doped with lithium acetate (LiOAc) were prepared by the solution cast technique. The molecular weight of PEO was 300 000 g mol(-1). Lithium acetate was added to PEO in different weight ratios ranging from 0 to 30 wt-%. The PEO-LiOAc mixtures were dissolved in 1% acetic acid solution and stirred overnight. The highest electrical conductivity obtained for this system is 2.18 x 10(-6) S cm(-1) for the sample containing 30 wt-% CH(3)COOLi. The conductivity-temperature study was carried out for all samples from 25 to 100 degrees C. Different amounts of ethylene carbonate were added as a plasticiser. This resulted in the conductivity increasing to 1.46 x 10(-5) S cm(-1). |
|---|